PA6 TSG-30 BK 9832 EMS-CHEMIE SUZHOU

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforcedThermal stabilityFiller: Glass fiber reinf30% filler by weight

Typical Applications:

Automotive ApplicationsElectrical/Electronic ApplicationsHome appliance componentssporting goodsIndustrial applicationsPower/Other ToolsConsumer product application fieldHousehold goodsEngineering accessoriesApplication in the automotive field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Electrical/Electronic Applications \| Home appliance components \| sporting goods \| Industrial applications \| Power/Other Tools \| Consumer product application field \| Household goods \| Engineering accessories \| Application in the automotive field
Properties:	Glass fiber reinforced \| Thermal stability \| Filler: Glass fiber reinf \| 30% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	kJ/m²	75	85
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	kJ/m²	65
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level	0.8mm		HB	--
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break	%	3.0	6.0
tensile strength	Break		175	MPa
Tensile modulus		MPa	9700	6000
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	cm/cm/°C	1.1E-04	--
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	cm/cm/°C	2E-05	--
Melting temperature		°C	260	--
Continuous use temperature	--4	°C	220	--
Continuous use temperature	Continuous use temperature	--3	°C	100to120	--
Hot deformation temperature	8.0MPa,Unannealed	°C	135	--
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	°C	220	--
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	%	2.0	--
Water absorption rate	Water absorption rate	Saturation,23°C	%	6.5	--
Shrinkage rate	MD	%	0.10	--
Shrinkage rate	Shrinkage rate	TD	%	0.70	--
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		kV/mm	25	24
Volume resistivity		ohms·cm	1E+14	1E+12
Surface resistivity		ohms	--
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test			210	MPa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.