Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| flow | | mm/mm | 25.4E-3-134.6E-3 |
| Water absorption rate | | % | 0.15-0.53 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 122to125 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield | | % | 1.5-5.0 |
| fracture | | | 56.0to260.0 Mpa |
| fracture | | | 26.0to260.0 Mpa |
| fracture | | % | 2.0-4.6 |
| fracture | | % | 1.7-2.7 |
| yield | | | 27.03to260.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | J/m | 0.085to0.462 |
| Charpy Notched Impact Strength | | kJ/m² | 0.789to3.762 |
| Impact strength of simply supported beam without notch | | kJ/m² | 7.892to21.357 |
| Impact strength of cantilever beam gap | | J/m | 0.013to0.050 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| dielectric strength | | V/mil | 490to610 |
| Surface Resistivity | | ohms | 1.0E+12-1.0E+14 |
| Volume resistivity | | ohms·cm | 1.0E+4-1.0E+16 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | mm/mm/°C | 30.5E-5到50.8E-5 |
| melting temperature | | °C | 220to265 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.