PP PP HC 30
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 1.06 g/cm³ | ||
| 1.06 g/cm³ | |||
| Shrinkage rate | 0.50到0.70 % | ||
| 0.50到0.70 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | Yield | 105 MPa | |
| Flexural modulus | 10000 MPa | ||
| Bending stress | 110 MPa | ||
| Tensile stress | Yield | 105 MPa | |
| Flexural modulus | 10000 MPa | ||
| Bending stress | 110 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 25 kJ/m² | ||
| 25 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | 1.1E+02 ohms | ||
| Volume resistivity | 1E+04 ohms·cm | ||
| Surface Resistivity | 1.1E+02 ohms | ||
| Volume resistivity | 1E+04 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 144 °C | |||
| melting temperature | 166 °C | ||
| 144 °C | |||
| melting temperature | 166 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.