Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | BS903 | 2.11 g/cm³ |
| Shrinkage rate | | | 0.50 % |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | BS903 | 100 % |
| Supporting hardness | | ASTMD2240 | 67 |
| tensile strength | | BS903 | 3.90 MPa |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| | | 350 Pa·s |
| Curing Time | | | <8.0 hr |
| TackFreeTime | | | 4.0 min |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| VolumetricExpansion | | | 4.9E-04 cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+14 ohms·cm |
| dielectric strength | | ASTMD149 | 20 kV/mm |
| dielectric constant | | ASTMD150 | 4.90 |
| Dissipation Factor | | ASTMD150 | 9E-04 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | | 1.6E-04 cm/cm/°C |
| thermal conductivity | | | 2.3 W/m/K |
| Service | | | -50到220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.