Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.45 % |
| Water absorption rate | | ISO 62 | 0.36 % |
| Shrinkage rate | | ISO 294-4 | 0.65 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 800 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 775775 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 800 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 12000 Mpa |
| tensile strength | | ISO 527-2/5 | 105 Mpa |
| Tensile strain | | ISO 527-2/5 | 1.7 % |
| Flexural modulus | | ISO 178 | 11000 Mpa |
| bending strength | | ISO 178 | 170 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | 3.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 25 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 1E+16 ohms |
| dielectric strength | | ASTM D149 | 16 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 0 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | | UL 746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| 0.45MPa, Unanealed, 64.0mm span | | ISO 75-2/Bf | 208 °C |
| 1.8MPa, Unanealed, 64.0mm span | | ISO 75-2/Af | 185 °C |
| vicat | | ISO 306/B120 | 205 °C |
| ball-indentation hardness | | IEC 60695-10-2 | PassPass |
| ball-indentation hardness | | IEC 60695-10-2 | Pass |
| Flow: -40 to 40 ° C | | ASTME831 | 3.1E-53.1E-5 cm/cm/°C |
| Flow: -30 to 80 ° C | | ISO 11359-2 | 3.5E-05 cm/cm/°C |
| Flow: 23 to 80 ° C | | ISO 11359-2 | 3.7E-05 cm/cm/°C |
| Horizontal: -40 to 40 ° C | | ASTME831 | 4.8E-54.8E-5 cm/cm/°C |
| Horizontal: -30 to 80 ° C | | ISO 11359-2 | 6E-05 cm/cm/°C |
| Horizontal: 23 to 80 ° C | | ISO 11359-2 | 7.3E-05 cm/cm/°C |
| thermal conductivity | | ISO 22007-2 | 0.80 W/m/K |
| thermal conductivity | | ISO 22007-2 | 1.11.1 W/m/K |
| thermal conductivity | | ISO 22007-2 | 1.31.3 W/m/K |
| thermal conductivity | | ISO 22007-2 | 1.5 W/m/K |
| 0.45MPa, Unanealed, 3.20mm | | ASTM D648 | 209 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.