PBT

PBT LONGLITE® PBT 7020-200X Chang Chun Plastics Co., Ltd. (CCP Group)

Properties:
Filler glass fiber reinforced material 20% filler by weight
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.5 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	23°C	ISO 178	155 MPa
Bending modulus	23°C	ISO 178	5300 MPa
Tensile strain	Break,23°C	ISO 527-2	2.8 %
tensile strength	Break,23°C	ISO 527-2	105 MPa
Tensile modulus	23°C	ISO 527-2	6000 MPa

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 11357-3	225 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	160 °C

Physical properties	Test Condition	Test Method	Test Result
Melt viscosity	260°C	ISO 11443	220 Pa·s
Shrinkage rate	MD	ISO 294-4	0.10to0.40 %
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.70to1.3 %
density		ISO 1183	1.38 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength	2.00mm	IEC 60243-1	20 kV/mm
Volume resistivity		IEC 60093	1E+14 ohms·cm
Surface resistivity		IEC 60093	1E+13 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.