PA/ABS NOVALLOY-A A2602 DAICEL JAPAN
106
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23℃ | % | 0.25到0.80 | ||
| Flow: 23 ℃ | mm/mm | 76.2E-3到127.0E-3 | ||
| Water absorption rate | 23℃,24hr | % | 0.70 | |
| 23℃ | g/cm³ | 1.12到1.20 | ||
| density | -- | 1.10到1.53 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 6.500到11.143 | |
| Charpy Notched Impact Strength | 23℃ | kJ/m² | 1.718到2.555 | |
| Impact strength of cantilever beam gap | 23℃ | J/m | 0.028到0.055 | |
| Rockwell hardness | 23℃ | 116到118 | ||
| 23℃ | MPa | 60.0到166.9 | ||
| elongation | 断裂,23℃ | % | 3.8到4.0 | |
| Fracture, 23 ℃ | MPa | 51.03到124.14 | ||
| 23℃ | MPa | 75.86到206.9 | ||
| Yield, 23 ℃ | MPa | 43.03到56.41 | ||
| 23℃ | MPa | 2551.72到6503.45 | ||
| Tensile modulus | 23℃ | MPa | 2503.45到5400.0 | |
| 23℃ | MPa | 2137.93到8344.83 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | °C | 107到181 | ||
| Hot deformation temperature | 1.8MPa,未退火 | °C | 106到202 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.