Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.34 g/cm³ |
| melt mass-flow rate | | ISO1133 | 1.0 g/10min |
| Shrinkage rate | | STM640808 | 0.97 % |
| Shrinkage rate | | STM640808 | 0.52 % |
| water content | | ISO960 | 0.15 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Hot filament ignition temperature | | IEC60695-2-13 | 960 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 6500 MPa |
| Tensile stress | Yield | ISO527-2 | 135 MPa |
| Tensile strain | Yield | ISO527-2 | 3.0 % |
| Flexural modulus | | ISO178 | 5700 MPa |
| Bending stress | | ISO178 | 190 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 45 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 50 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | 1E+17 ohms·cm |
| dielectric strength | | IEC60243-1 | 70 kV/mm |
| CTI | | IEC60112 | 550 V |
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 240 °C |
| vicat | | ISO306/B | 250 °C |
| | ISO3146 | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare