Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | Hardener | | 按重量计算的混合比:30 |
| Thermosetting components | | | 4.0to8.0 hr |
| Thermosetting components | Resin | | 100 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.10to1.16 g/cm³ |
| Viscosity | | | 0.25to0.35 Pa·s |
| Curing Time | | | 16to24 hr |
| STORAGE STABILITY | | | 55to65 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 7619 | 83to87 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ISO 178 | 120 MPa |
| compression stress | | ISO 604 | 90.0to110 MPa |
| Flexural modulus | | ISO 178 | 2700to3300 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 50to70 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 94.0to100 °C |
| Glass Transition Temperature | | DSC | 90.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.