Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| ash content | | ASTM D2584 | 18to22 % |
| density | | ASTM D792 | 1.10 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 3.0to7.0 g/10min |
| Shrinkage rate | | ASTM D955 | 1.1 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | >38 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 30.0 MPa |
| elongation | Break | ASTM D638 | 8.0 % |
| Flexural modulus | | ASTM D790 | 2700 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | >1.0E+14 ohms·cm |
| dielectric strength | | ASTM D149 | 40 kV/mm |
| Dissipation Factor | | ASTM D150 | 2E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 110 °C |
| Heat distortion temperature | | ASTM D648 | 68.0 °C |
| vicat | | ASTM D15252 | 140 °C |
| melting temperature | | ASTM D2117 | 160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare