Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.40 % |
| Shrinkage rate | | ASTM D955 | 0.50 % |
| Water absorption rate | | ASTM D570 | 1.1 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2060 Mpa |
| Tensile modulus | | ISO 527-2/1 | 2010 Mpa |
| tensile strength | | ASTM D638 | 39.0 Mpa |
| tensile strength | | ISO 527-2/5 | 38.0 Mpa |
| tensile strength | | ASTM D638 | 36.0 Mpa |
| tensile strength | | ISO 527-2/5 | 31.0 Mpa |
| elongation | | ASTM D638 | 3.1 % |
| elongation | | ISO 527-2/5 | 3.0 % |
| elongation | | ASTM D638 | 6.0 % |
| elongation | | ISO 527-2/5 | 24 % |
| Flexural modulus | | ASTM D790 | 2090 Mpa |
| Flexural modulus | | ISO 178 | 1980 Mpa |
| Bending stress | | ISO 178 | 59.0 Mpa |
| Bending stress | | ASTM D790 | 65.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| | ASTM D4812, ISO 180/1U | 无断裂 |
| Dart impact equipped with measuring instruments | | ASTM D3763 | 32.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 1.0E+9 到 1.0E+11 ohms |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 70 到 80 °C |
| drying time | | | 4.0 hr |
| Suggested maximum moisture content | | | 0.050 到 0.10 % |
| Temperature at the rear of the barrel | | | 180 到 195 °C |
| Temperature in the middle of the barrel | | | 195 到 205 °C |
| Temperature at the front of the material cylinder | | | 205 到 215 °C |
| Processing (melt) temperature | | | 200 到 210 °C |
| Temperature | | | 10 到 50 °C |
| Back pressure | | | 0.200 到 0.300 Mpa |
| screw speed | | | 30 到 60 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648 | 88.0 °C |
| Thermal deformation temperature under load | | ISO 75-2/Bf | 91.0 °C |
| Thermal deformation temperature under load | | ASTM D648 | 76.0 °C |
| Thermal deformation temperature under load | | ISO 75-2/Af | 76.0 °C |
| | ASTM E831 | 9.3E-5 cm/cm/°C |
| | ISO 11359-2 | 9.3E-5 cm/cm/°C |
| | ASTM E831 | 1.0E-4 cm/cm/°C |
| | ISO 11359-2 | 1.0E-4 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.