Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.32 g/cm³ |
| density | | ASTM D792 | 1.32 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 113 |
| Rockwell hardness | R-Scale | ASTM D785 | 113 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ASTM D1003 | 4.0 % |
| Transmittance | | ASTM D1003 | 84.0 % |
| Transmittance | | ASTM D1003 | 84.0 % |
| Haze ratio | | ASTM D1003 | 4.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| EquilibriumTorque | | 内部方法 | 13.7 J |
| stability time | | 内部方法 | 36.0 min |
| EquilibriumTorque | | 内部方法 | 13.7 J |
| stability time | | 内部方法 | 36.0 min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 75.8 MPa |
| Tensile modulus | | ASTM D638 | 2650 MPa |
| tensile strength | Yield | ASTM D638 | 46.9 MPa |
| bending strength | | ASTM D790 | 75.8 MPa |
| Tensile modulus | | ASTM D638 | 2650 MPa |
| tensile strength | Yield | ASTM D638 | 46.9 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 130 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 130 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 800 J/m |
| Impact strength of cantilever beam gap | | ASTM D1822 | 168 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 800 J/m |
| Impact strength of cantilever beam gap | | ASTM D1822 | 168 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 60.0 °C |
| Heat distortion temperature | | ASTM D648 | 60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.