PBT SK602-BK851 DUPONT KOREA

Form：Granules | Grade：Injection grade

Properties:

Flame retardantGlass fiber reinforcedFiller: Glass fiber reinf15% filler by weight15% filler by weight

Typical Applications:

Automotive ApplicationsElectronic and electrical components

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Electronic and electrical components
Properties:	Flame retardant \| Glass fiber reinforced \| Filler: Glass fiber reinf \| 15% filler by weight \| 15% filler by weight

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.0	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	40	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Fogging-G-value	condensate	ISO 6452	1E-04	g
FMVSS flammability		FMVSS302	B
UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	HB
	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	3.0mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	HB
Burning rate	1.00mm	ISO 3795	30	mm/min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break	ISO 527-2	3.5	%
tensile strength	Break	ISO 527-2	109	Mpa
Tensile modulus		ISO 527-2	5800	Mpa
Tensile modulus	Tensile modulus	0.00 mm, 23 ℃, Injection Molded	ISO 527-1	5700	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.50 mm	UL 94	HB
	UL flame retardant rating	3.00 mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	6.00 mm	UL 94	HB
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	200	°C
Melting temperature		ISO 11357-3	225	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Top out temperature			170	°C
Shrinkage rate	MDLength2(2.00mm)	ISO 294-4	360	mm
	Shrinkage rate	MD	ISO 294-4	0.40	%
	Shrinkage rate	Shrinkage rate	TD	ISO 294-4	1.1	%
density		ISO 1183	1.41	g/cm³
density	density		ISO 1183	1.41	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	IEC 60250	0.017
Dissipation factor	Dissipation factor	100Hz	IEC 60250	7E-04
Compared to the anti leakage trace index		IEC 60112	PLC 3
Surface resistivity		IEC 60093	1E+14	ohms
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	35	KV/mm
Relative permittivity	100Hz	IEC 60250	3.70
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.60
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Odor		VDA270	3.00
EmissionofOrganicCompounds		VDA277	140	µgC/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.