ABS PA-707 TAIWAN CHIMEI

126

Form：Granules | Grade：Injection grade

Properties:

High rigidityHigh gloss

Typical Applications:

Lighting fixturesOffice suppliesElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(12)

Datasheet

Alternative Model(3)

Product Description

Typical Applications:	Lighting fixtures \| Office supplies \| Electronic field \| Electrical field
Properties:	High rigidity \| High gloss

Certificates

MSDS

RoHS

SGS

TDS

MSDS

RoHS

SVHC

Processing

Statement

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
remarks			-
characteristic			高光泽性高刚性。
Color			-
purpose			电话机外壳 / 灯座 / 玩具 / 办公室用品 / 时钟外壳 / 家电按钮
machinability	Test Condition	Test Method	Test Result	Test Unit
Dry conditions			80°C下烘料約2-3小時
Processing temperature			180-220	°C
	Processing temperature			190-230	°C
	Processing temperature	Processing temperature			-	°C
Screw speed			-	rpm
Mold temperature			30-70°C	°C
Melt Temperature			-	°C
pressure			-	Mpa
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap		ASTM D256/ISO 179	13（2.4）	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	-	%
Tensile modulus		ASTM D638/ISO 527	-	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	520（7380）	kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	15	%
Rockwell hardness		ASTM D785	R-116
Bending modulus		ASTM D790/ISO 178	29000（41000）	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	860（12.200）	kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength		ASTM D256/ISO 179	-	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap		ASTM D256/ISO 179	-	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	15（2.6)	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	-	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	1.6mmHB
Hot deformation temperature	HDT	ASTM D648/ISO 75	99(210)	℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	88(190)	℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	105(221)	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	-	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.06
Shrinkage rate		ASTM D955	-	%
Water absorption rate		ASTM D570/ISO 62	-	%
melt mass-flow rate		ASTM D1238/ISO 1133	1.7	g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	23	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.