PPS 1140L7 SD3002 CELANESE USA

Form：Granules | Grade：Injection grade

Properties:

Flame retardantGlass fiber reinforcedHigh temperature resistan

Typical Applications:

fibreBottle cap

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	fibre \| Bottle cap
Properties:	Flame retardant \| Glass fiber reinforced \| High temperature resistan

Certificates

No Data...

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.38 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.5 mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1A	14500	Mpa
tensile strength	Break	ISO 527-2/1A/5	170	Mpa
Tensile strain	Break	ISO 527-2/1A/5	1.6	%
Bending modulus	23°C	ISO 178	14500	Mpa
bending strength		ISO 178	260	Mpa
Compressive modulus		ISO 604	14000	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			130 to 140	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Hopper temperature			20 to 30	°C
Temperature at the rear of the barrel			290 to 300	°C
Temperature in the middle of the barrel			310 to 320	°C
Temperature at the front of the material cylinder			330 to 340	°C
Spray nozzle temperature			310 to 330	°C
Processing (melt) temperature			330 to 340	°C
Mold temperature			140 to 160	°C
Injection speed			快速
Back pressure			< 3.00	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	270	°C
Hot deformation temperature	Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	200	°C
Glass transition temperature		ISO 11357-2	90.0	°C
Melting temperature		ISO 11357-3	280	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	横向Flow	ISO 294-4	0.50 - 0.70	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.10 - 0.30	%
Water absorption rate	Saturation, 23°C	ISO 62	0.020	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	> 1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	26	KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 4
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M -Sale	ISO 2039-2	100

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.