PAR U-POLYMER AXG-1500-30
177
- Properties:Filler: Glass fiber reinf30% filler by weight
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | % | 0.35 -- | |
| % | 0.70 -- | ||
| Water absorption rate | % | 0.26 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | 121 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | MPa | 143 112 | |
| elongation | % | 4.0 6.0 | |
| Flexural modulus | MPa | 8200 6300 | |
| bending strength | MPa | 211 181 | |
| compressive strength | MPa | 147 -- |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ohms·cm | -- | |
| dielectric strength | kV/mm | -- | |
| dielectric constant | 3.60 -- | ||
| Dissipation Factor | -- | ||
| arc resistance | sec | 60.0 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | °C | 179 -- | |
| Linear coefficient of thermal expansion | cm/cm/°C | 4.6E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.