| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.01 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 24 g/10min |
| melt mass-flow rate | | ASTM D1238 | 27 g/10min |
| Shrinkage rate | | ASTM D955 | 0.95 % |
| Shrinkage rate | | ASTM D955 | 0.75 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 84 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 750 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 750 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| fracture | | ASTM D638 | 6.00 MPa |
| fracture | | ISO 527-2/50 | 7.00 MPa |
| fracture | | ASTM D638 | 150 % |
| fracture | | ISO 527-2/50 | 180 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 7.1E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | <-40.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.