PP Homopolymer Polifil® PP M-20
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 8.0to12 g/10min | |
| Shrinkage rate | ASTM D955 | 1.1 % | |
| density | ASTM D792 | 1.05 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 96 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2480 MPa | |
| tensile strength | ASTM D638 | 31.0 MPa | |
| elongation | ASTM D638 | 4.0 % | |
| ASTM D638 | 8.0 % | ||
| Flexural modulus | ASTM D790 | 3190 MPa | |
| bending strength | ASTM D790 | 42.1 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 51 J/m | |
| GardnerImpact | ASTM D3029 | 0.678 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ASTM D648 | 127 °C | |
| ASTM D648 | 82.2 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.