| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.68 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.60 % |
| Shrinkage rate | | ISO 294-4 | 0.50 % |
| Water absorption rate | | ISO 62 | >0.020 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 92 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Flowability | | 内部方法 | 136 mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 140 MPa |
| Tensile strain | Break | ISO 527-2 | 1.8 % |
| Flexural modulus | | ISO 178 | 11700 MPa |
| bending strength | | ISO 178 | 226 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | IEC 60250 | 1.9E-03 |
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric constant | | IEC 60250 | 3.60 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 265 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.6E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5.3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.