PPS 1140L4 SD3002 CELANESE USA

Form：Granules | Grade：Injection grade

Properties:

Flame retardantHigh temperature resistanenhanceGlass fiber reinforcedInjection gradeMedium melt viscosity

Typical Applications:

Fiber gradeDuring injection moldingSlight flash

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Fiber grade \| During injection molding \| Slight flash
Properties:	Flame retardant \| High temperature resistan \| enhance \| Glass fiber reinforced \| Injection grade \| Medium melt viscosity

Certificates

No Data...

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
SpecificHeatCapacity of Melt		Internal Method	1500	J/kg/°C
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	53	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	53	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	10	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	34	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	3.0mm	UL 94	5VA
	UL flame retardant rating	UL flame retardant rating	0.38mm	UL 94	V-0
Extreme Oxygen Index		ISO 4589-2	47	%
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM-D570	0.02	%
density		ISO 1183	1.65	g/cm³
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	285	Mpa
Bending modulus	23°C	ISO 178	14500	Mpa
elongation	Break	ISO 527-2/1A/5	1.9	%
elongation	elongation	Break,23°C	ASTM D638	1.7	%
tensile strength	Break	ISO 527-2/1A/5	195	Mpa
tensile strength	tensile strength	Break,23°C	ASTM D638	200	Mpa
Rockwell hardness		ASTM-D785	100	R-Scale
Impact strength of cantilever beam gap		ISO 180/1A	10	kJ/m²
Bending modulus		ISO 178	14500	Mpa
bending strength		ISO 178	285	Mpa
Tensile modulus		ISO 527	14700	Mpa
tensile strength		ISO 527	195	Mpa
Tensile modulus	-40°C	ASTM D638	14500	Mpa
	Tensile modulus	75°C	ASTM D638	11900	Mpa
		Tensile modulus	150°C	ASTM D638	4270	Mpa
			Tensile modulus	200°C	ASTM D638	3240	Mpa
			Tensile modulus	Tensile modulus	--	ISO 527-2/1A/1	14700	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	4.2E-05	cm/cm/°C
UL flame retardant rating		UL 94	V-0
Hot deformation temperature	1.80Mpa	ISO 75-A	270	°C
	Hot deformation temperature	0.45MPa,Annealed	ASTM D648	280	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	265	°C
			Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	270	°C
			Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	215	°C
Glass transition temperature		ISO 11357-2	90.0	°C
Melting temperature		ISO 11357-3	280	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2.6E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ISO 294-4	0.2-0.6	%
	Shrinkage rate	TD	ISO 294-4	0.40-0.60	%
	Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.20-0.60	%
Water absorption rate	Saturation,23°C	ISO 62	0.020	%
Specific volume		ASTM D792	0.611	cm³/g
Shrinkage rate	MD	ASTM D955	0.20-0.30	%
density		ASTMD792	1.65	g/cm³
Shrinkage rate	TD	ASTM D955	0.50-0.70	%
Biochemical properties	Test Condition	Test Method	Test Result	Test Unit
Filling amount			40	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	--	ASTM D257	1E+16	ohms·cm
Volume resistivity	Volume resistivity	--	IEC 60093	>1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	28	KV/mm
Dielectric constant	1kHz	ASTM D150	3.50
Surface resistivity		IEC 60093	>1.0E+15	ohms
Dielectric constant	1MHz	ASTM D150	3.50
Dielectric constant	Dielectric constant	1MHz	IEC 60250	4.60
Dissipation factor	1kHz	ASTM D150	1E-03
	Dissipation factor	1MHz	ASTM D150	1E-03
	Dissipation factor	Dissipation factor	1MHz	IEC 60250	6.2E-03
Arc resistance		ASTM D495	134	sec
Compared to the anti leakage trace index		IEC 60112		V
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ASTM D785	100
Rockwell hardness	Rockwell hardness	M-Sale	ISO 2039-2	100
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		Internal Method	3.18	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.