Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.15 g/cm³ |
| melt mass-flow rate | | ISO1133 | 8.0 g/10min |
| Shrinkage rate | | ISO294-4 | 0.30到0.50 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 115 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 30 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180 | 10 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2/50 | 73.0 MPa |
| Tensile strain | Break | ISO527-2/50 | 5.0 % |
| Flexural modulus | | ISO178 | 5000 MPa |
| Bending stress | | ISO178 | 110 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 117 °C |
| vicat | | ISO306/B50 | 120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare