HDPE 1000-B1600

Properties:
Product features
high flow modified ultra-high molecular weight polyethylene
greatly improving flowability while maintaining its original performance
especially in the fields of anti-corrosion
wear resistance
self-lubrication
etc. It can replace fluoroplastics such as polytetrafluoroethylene. 1. It can continuously and quickly extrude wear-resistant slide rails
profiles
sheets
pipelines on ordinary extruders. 2. It can inject self-lubricating wear-resistant shaft sleeves
conveyor belt idlers
and slides on ordinary injection machines?
Usages:
Suitable for injection
extrusion
and compression
Compare

Technical Data Sheet

Basic performance	Test Condition	Test Method	Test Result
density			0.945 g/cm3
melt mass-flow rate			0.50 g/10min

Mechanical properties	Test Condition	Test Method	Test Result
Shore hardness			57
bending strength			15.2 MPa
tensile strength			24.68 MPa
Charpy Notched Impact Strength			110 kJ/m2
elongation at break			>340 %
Flexural modulus			800-1100 MPa
Impact strength of cantilever beam gap			65.29 kJ/m2

Other performance	Test Condition	Test Method	Test Result
Wear factor			0.15 %

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature			83.1 ℃
brittle temperature			-80 ℃

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.