PA66 A217-1 NAT BASF KOREA

Form：Granules

Properties:

Thermal stabilityEasy electroplating

Typical Applications:

Laptop caseElectrical applicationsAutomotive ApplicationsApplication in the automotive field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Laptop case \| Electrical applications \| Automotive Applications \| Application in the automotive field
Properties:	Thermal stability \| Easy electroplating

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-2	26	%
UL flame retardant rating		NFF16-101	F2
Ignition temperature of heating wire	1.6mm	IEC 60695-2-13	650	°C
Burning wire flammability index	1.6mm	IEC 60695-2-12	650	°C
Burning wire flammability index	Burning wire flammability index	0.8mm	IEC 60695-2-12	650	°C
UL flame retardant rating	3.2mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	V-2
smoke density		NFF16-101	I3
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C	ISO 178	130	Mpa
bending strength	bending strength	23°C	ASTM D790	125	Mpa
Bending modulus	23°C	ISO 178	3100	Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	3500	Mpa
Tensile strain	Break,23°C	ISO 527-2	>30	%
elongation	Break,23°C	ASTM D638	30	%
Tensile strain	Yield,23°C	ISO 527-2	4.5	%
tensile strength	Break,23°C	ISO 527-2/1A	60.0	Mpa
	tensile strength	Yield,23°C	ISO 527-2/1A	95.0	Mpa
	tensile strength	tensile strength	Yield,23°C	ASTM D638	85.0	Mpa
Tensile modulus	23°C	ISO 527-2/1A	3500	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	220	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	210	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	75.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	75.0	°C
Melting temperature		ISO 11357-3	262	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.9	%
Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	1.3	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 1
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Dissipation factor		IEC 60250	0.030
Relative permittivity		IEC 60250	2.90
Dielectric strength	2.00mm	IEC 60243-1	25	KV/mm
Surface resistivity		IEC 60093	1E+15	ohms
Volume resistivity		IEC 60093	1E+15	ohms·cm
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
EuropeanRailwaysCertifications	R22	EN45545-2	HL2
EuropeanRailwaysCertifications	EuropeanRailwaysCertifications	R23	EN45545-2	HL2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.