| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.32 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.40 % |
| Water absorption rate | | ASTM D570 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 110 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 51 J/m |
| Impact strength of cantilever beam gap | | ASTM D4218 | NoBreak |
| Impact strength of cantilever beam gap | | ASTM D4218 | NoBreak |
| Impact strength of cantilever beam gap | | ASTM D256 | 36 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 57.0 MPa |
| tensile strength | | ASTM D638 | 26.0 MPa |
| elongation | | ASTM D638 | 4.0 % |
| Flexural modulus | | ASTM D790 | 2500 MPa |
| bending strength | | ASTM D790 | 81.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTM D150 | 8E-03 |
| dielectric strength | | ASTM D149 | 16 kV/mm |
| dielectric constant | | ASTM D150 | 3.20 |
| dielectric constant | | ASTM D150 | 3.00 |
| Dissipation Factor | | ASTM D150 | 0.020 |
| arc resistance | | ASTM D495 | 155 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 66.0 °C |
| Heat distortion temperature | | ASTM D648 | 62.0 °C |
| vicat | | ASTM D15252 | 79.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.