'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PBT V4860HR SABIC INNOVATIVE US
100
Form：Granules | Grade：Injection grade
Properties:
High rigidityGlass fiber reinforced
Typical Applications:
Electrical applicationsAutomotive Applications
Product Description
Certificates(1)
Datasheet
Product Description
| Typical Applications: | Electrical applications | Automotive Applications |
| Properties: | High rigidity | Glass fiber reinforced |
Certificates
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.5 | kJ/m² |
| 23°C | ASTM D256 | 90 | J/m | |
| -30°C | ASTM D256 | 74 | J/m | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 | kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 13.4 | J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.8mm | UL 94 | V-0 | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | Break | ISO 527-2/5 | 111 | Mpa |
| elongation | Yield | ASTM D638 | 2.3 | % |
| Fracture bending strain | ISO 178 | 2.9 | % | |
| bending strength | Break,50.0mmSpan | ASTM D790 | 2.96 | Mpa |
| Yield,50.0mmSpan | ASTM D790 | 174 | Mpa | |
| Tensile strain | Yield | ISO 527-2/5 | 2.1 | % |
| elongation | Break | ASTM D638 | 2.3 | % |
| Tensile strain | Break | ISO 527-2/5 | 2.2 | % |
| Bending modulus | 50.0mmSpan | ASTM D790 | 6740 | Mpa |
| ISO 178 | 7880 | Mpa | ||
| bending strength | --6 | ISO 178 | 182 | Mpa |
| --7 | ISO 178 | 183 | Mpa | |
| tensile strength | Break | ASTM D638 | 115 | Mpa |
| Yield | ISO 527-2/5 | 112 | Mpa | |
| Yield | ASTM D638 | 116 | Mpa | |
| Tensile modulus | ISO 527-2/1 | 9450 | Mpa | |
| ASTM D638 | 9750 | Mpa | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO 11359-2 | 1.2E-04 | cm/cm/°C |
| TD：-40to95°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| MD：23to80°C | ISO 11359-2 | 2.3E-05 | cm/cm/°C | |
| MD：-40to95°C | ASTME831 | 2.4E-05 | cm/cm/°C | |
| Ball Pressure Test | 75°C | IEC 60695-10-2 | Pass | |
| Vicat softening temperature | -- | ISO 306/B120 | 175 | °C |
| -- | ISO 306/B50 | 176 | °C | |
| ASTM D152512 | 176 | °C | ||
| Hot deformation temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 188 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTM D648 | 205 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTM D648 | 197 | °C | |
| 0.45MPa,Unannealed,6.40mm | ASTM D648 | 221 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| density | ISO 1183 | 1.64 | g/cm³ | |
| ASTM D792 | 1.64 | g/cm³ | ||
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.060 | % |
| Saturation,23°C | ISO 62 | 0.19 | % | |
| Shrinkage rate | TD：3.20mm | Internal Method | 0.50-1.0 | % |
| MD：3.20mm | Internal Method | 0.50-0.70 | % | |
| Melt Volume Flow Rate (MVR) | 250°C/5.0kg | ISO 1133 | 12.4 | cm3/10min |
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 18 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.