TPU-Ether Estane® 2103-90AEFH TPU
0
- Usages:film
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.40to0.50 % | |
| ASTM D955 | 0.50to0.80 % | ||
| density | ASTM D792 | 1.14 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 6.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | Shore A | ASTM D2240 | 92 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Taber abraser | ASTM D1044 | 50.0 mg |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ASTM D412 | 520 % | |
| elongation at break | ASTM D412 | 60 % | |
| tear strength | ASTM D624 | 94.6 kN/m | |
| compression set | ASTM D395B | 25 % | |
| ASTM D395B | 40 % | ||
| tensile strength | ASTM D412 | 7.00 MPa | |
| ASTM D412 | 9.90 MPa | ||
| ASTM D412 | 18.6 MPa | ||
| ASTM D412 | 35.5 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glass Transition Temperature | DSC | -27.0 °C | |
| vicat | ASTM D15252 | 102 °C | |
| Linear coefficient of thermal expansion | ASTM D696 | 1.6E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.