PC HF1110-111J SABIC INNOVATIVE JAPAN

Form：Granules | Grade：Injection grade

Properties:

High mobilityHigh temperature resistantransparent

Typical Applications:

Electronic and electrical accessoriesAutomotive components

Supplier(0)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Electronic and electrical accessories \| Automotive components
Properties:	High mobility \| High temperature resistan \| transparent

Certificates

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	2540 μm	ASTM D1003	88.0	%
turbidity	2540 μm	ASTM D1003	1.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Energy at Peak	ASTM D3763	54.0	J
Impact strength of cantilever beam gap		ASTM D1822	378	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.1 mm	UL 94	V-2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ASTM D638	62.0	Mpa
tensile strength	tensile strength	Break	ASTM D638	65.0	Mpa
elongation	Break	ASTM D638	120	%
Bending modulus	50.0 mm Span	ASTM D790	2300	Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	93.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			120	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			40 to 60	%
Temperature at the rear of the barrel			250 to 270	°C
Temperature in the middle of the barrel			260 to 280	°C
Temperature at the front of the material cylinder			270 to 295	°C
Spray nozzle temperature			265 to 290	°C
Processing (melt) temperature			270 to 295	°C
Mold temperature			70 to 95	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
Exhaust hole depth			0.025 to 0.076	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	126	°C
RTI Elec		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI		UL 746	130	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	25	g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70	%
Water absorption rate	24 hr	ASTM D570	0.10	%
	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.35	%
	Water absorption rate	Water absorption rate	Equilibrium, 100°C	ASTM D570	0.58	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		UL 746	PLC 2
High arc combustion index		UL 746	PLC 1
High voltage arc tracing rate		UL 746	PLC 2
Hot wire ignition		UL 746	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.