Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD1505 | 1.10到1.12 g/cm³ |
| Water absorption rate | | ASTMD570 | <0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 85 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | | 1.661 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Hydrogen | | ASTMD1434 | 210 cm³·mm/m²/atm/24hr |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| | ASTMD1894 | 0.25 |
| | ASTMD1894 | 0.25 |
| film | Test Condition | Test Method | Test Result |
|---|
| Secant modulus MD | | ASTMD882 | 2410 MPa |
| tensile strength | Yield | ASTMD882 | 42.1 MPa |
| tensile strength | Break | ASTMD882 | 48.3 MPa |
| elongation | Yield | ASTMD882 | 2.5 % |
| elongation | Break | ASTMD882 | <250 % |
| oxygen permeability | | ASTMD1434 | 15 cm³·mm/m²/atm/24hr |
| Water vapor permeability | | ASTME96 | 0.59 g·mm/m²/atm/24hr |
| CarbonDioxidePermeability | | ASTMD1434 | 84 cm³·mm/m²/atm/24hr |
| NitrogenPermeability | | ASTMD1434 | 3.0 cm³·mm/m²/atm/24hr |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | 1E+13 ohms |
| dielectric constant | | ASTMD150 | 2.65 |
| Dissipation Factor | | ASTMD150 | 2E-04 |
| Dissipation Factor | | ASTMD150 | 2E-04 |
| Dissipation Factor | | ASTMD150 | 6E-04 |
| Volume resistivity | | ASTMD257 | 1.4E+17 ohms·cm |
| dielectric strength | | ASTMD149 | 280 kV/mm |
| dielectric constant | | ASTMD150 | 2.65 |
| dielectric constant | | ASTMD150 | 2.65 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | DSC | 420 °C |
| | TMA | 6.9E-05 cm/cm/°C |
| specific heat | | | 837 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.13 W/m/K |
| Service | | | 80 °C |
| Continuous use temperature | | | 60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.