Technical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 密度 | | ASTMD792 | 1.29 g/cm³ |
| 熔体质量流动速率 | 365°C/5.0kg | ASTMD1238 | 20to28 g/10min |
| 收缩率 | MD：3.18mm | ASTMD955 | 0.70 % |
| 吸水率 | 24hr | ASTMD570 | 0.37 % |
| 吸水率 | 平衡 | ASTMD570 | 1.1 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 热变形温度 | 1.8MPa,未退火,3.18mm | ASTMD648 | 207 °C |
| 玻璃转化温度2 | | DSC | 220 °C |
| 线性热膨胀系数 | MD：3.18mm | ASTMD696 | 5.6E-05 cm/cm/°C |
| 补充信息 | Test Condition | Test Method | Test Result |
|---|
| SteamSterilization-w/Morpholine4 | | | >1000 cycles |
| 光学性能 | Test Condition | Test Method | Test Result |
|---|
| 折射率 | | ASTMD542 | 1.672 |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| FlameRating3 | 0.76mm | UL94 | V-0 |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 拉伸强度 | 3.18mm | ASTMD638 | 69.6 Mpa |
| 伸长率 | 屈服,3.18mm | ASTMD638 | 7.2 % |
| 伸长率 | 断裂,3.18mm | ASTMD638 | 60to120 % |
| 弯曲模量 | 3.17mm | ASTMD790 | 2410 Mpa |
| FlexuralStrength | 5.0%Strain,3.18mm | ASTMD790 | 91.0 Mpa |
| 拉伸模量 | 3.18mm | ASTMD638 | 2340 Mpa |
| 电气性能 | Test Condition | Test Method | Test Result |
|---|
| VolumeResistivity | 3.18mm | ASTMD257 | 9E+15 ohms·cm |
| 介电强度 | 0.0254mm | ASTMD149 | >200 KV/mm |
| 介电强度 | 3.18mm | ASTMD149 | 15 KV/mm |
| DielectricConstant | 3.18mm,60Hz | ASTMD150 | 3.44 |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|
| 悬壁梁缺口冲击强度 | 3.17mm | ASTMD256 | 690 J/m |
| TensileImpactStrength | 3.18mm | ASTMD1822 | 399 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.