Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO294-4 | 0.10到0.20 % |
| density | | ISO1183 | 1.45 g/cm³ |
| Melt volume flow rate | | ISO1133 | 3.00 cm³/10min |
| Shrinkage rate | | ISO294-4 | 0.20到0.30 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 825 °C |
| UL flame retardant rating | | UL94 | V-2 |
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Yield | ISO527-2/5 | 2.9 % |
| Tensile strain | Break | ISO527-2/5 | 3.0 % |
| Tensile modulus | | ISO527-2/1 | 12100 MPa |
| Tensile stress | Yield | ISO527-2/5 | 109 MPa |
| Tensile stress | Break | ISO527-2/5 | 107 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 12 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 12 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 42 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 43 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC60093 | >1.0E+17 ohms·cm |
| dielectric strength | | IEC60243-1 | 41 kV/mm |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 160 °C |
| | ISO75-2/A | 154 °C |
| vicat | | ISO306/B50 | 150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.