| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO1133 | 8.50 cm³/10min |
| Shrinkage rate | | ISO294-4 | 1.5 % |
| Shrinkage rate | | ISO294-4 | 1.5 % |
| Water absorption rate | | ISO62 | 0.70 % |
| Water absorption rate | | ISO62 | 0.60 % |
| melt mass-flow rate | | ISO1133 | 8.5 g/10min |
| Water absorption rate | | ISO62 | 0.20 % |
| density | | ISO1183 | 1.19 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 55 |
| | ISO868 | 52 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | IEC60695-11-10,-20 | HB |
| UL flame retardant rating | | IEC60695-11-10,-20 | HB |
| Limiting Oxygen Index | | ISO4589-2 | 20 % |
| FMVSS flammability | | FMVSS302 | SE |
| Fogging-G-value | | ISO6452 | 1E-04 g |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 190 MPa |
| Tensile stress | Yield | ISO527-2 | 15.0 MPa |
| Tensile stress | Break | ISO527-2 | 35.0 MPa |
| Tensile stress | | ISO527-2 | 6.90 MPa |
| Tensile stress | | ISO527-2 | 11.1 MPa |
| Tensile stress | | ISO527-2 | 14.7 MPa |
| Tensile stress | | ISO527-2 | 16.0 MPa |
| Tensile strain | Yield | ISO527-2 | 36 % |
| Tensile strain | Break | ISO527-2 | >300 % |
| Nominal tensile fracture strain | | ISO527-2 | 640 % |
| TensileCreepModule | | ISO899-1 | 140 MPa |
| Tensile creep modulus | | ISO899-1 | 100 MPa |
| Flexural modulus | | ISO178 | 195 MPa |
| abrasion resistance | | ISO4649 | 120 mm³ |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Tensile impact strength | | ISO8256/1 | 300 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | Across Flow | ISO34-1 | 120 kN/m |
| tear strength | | ISO34-1 | 130 kN/m |
| compression set | | ISO815 | 60 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| EffectiveThermal Diffusivity | | | 5.44E-08 m²/s |
| vicat | | ISO306/A50 | 177 °C |
| vicat | | ISO306/B50 | 75.0 °C |
| melting temperature | | ISO11357-3 | 201 °C |
| | ISO11359-2 | 1.8E-04 cm/cm/°C |
| | ISO11359-2 | 1.8E-04 cm/cm/°C |
| Heat distortion temperature | | ISO75-2/B | 78.0 °C |
| Heat distortion temperature | | ISO75-2/A | 51.0 °C |
| brittle temperature | | ISO974 | -80.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.