COC 9506F04 CELANESE GERMANY
1549
- Properties:Chemical resistanceantioxidantHydrolysis resistance
- Usages:Bottle capElectrical applicationsfilm
Compare
View PricesTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 熔体体积流动速率 | 190°C/2.16kg | ISO1133 | 1.00 cm3/10min |
| 230°C/2.16kg | ISO1133 | 6.00 cm3/10min | |
| 吸水率 | 饱和,23°C | ISO62 | 0.010 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 玻璃转化温度3 | ISO11357-2 | 65.0 °C |
| 光学性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 光泽度 | 60° | ISO2813 | >100 |
| 雾度 | ISO14782 | <1.0 % |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 拉伸模量 | ISO527-2/1A/1000 | 2600 Mpa |
| 薄膜 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 拉伸模量 | MD | ISO527-3 | 1700 Mpa |
| TD | ISO527-3 | 2000 Mpa | |
| 拉伸应力 | MD:断裂 | ISO527-3 | 55.0 Mpa |
| TD:断裂 | ISO527-3 | 55.0 Mpa | |
| 伸长率 | MD:断裂 | ISO527-3 | 2.9 % |
| TD:断裂 | ISO527-3 | 3.6 % | |
| 落锤冲击 | ISO7765-1 | <36 g | |
| 埃尔曼多夫抗撕强度 | MD | ISO6383-2 | 2.3 N |
| TD | ISO6383-2 | 2.4 N | |
| 透氧率 | 23°C,50%RH | ASTMD3985 | 17 cm³·mm/m²/atm/24hr |
| WaterVaporPermeability2 | 38°C | ISO15106-3 | 0.800 g·100µm/(m²·day |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.