elastomer	Test Condition	Test Method	Test Result	Test Unit
tensile strength	100%Strain	ASTM D412	8.89	MPa
	tensile strength	300%Strain	ASTM D412	17.7	MPa
	tensile strength	tensile strength	Yield	ASTM D412	59.3	MPa
Shore hardness		ASTM D2632	38	%
tensile strength	100%Strain	ASTM D412	22.1	MPa
	tensile strength	300%Strain	ASTM D412	57.9	MPa
	tensile strength	tensile strength	Yield	ASTM D412	57.9	MPa
elongation	Break	ASTM D412	300	%
Permanent compression deformation		ASTM D395B	36	%
Shore hardness		ASTM D2632	52	%
tensile strength	100%Strain	ASTM D412	2.28	MPa
tensile strength	tensile strength	300%Strain	ASTM D412	3.24	MPa
Permanent compression deformation		ASTM D395B	42	%
tensile strength	Yield	ASTM D412	38.6	MPa
elongation	Break	ASTM D412	500	%
Permanent compression deformation		ASTM D395B	24	%
Shore hardness		ASTM D2632	36	%
tensile strength	100%Strain	ASTM D412	33.1	MPa
tensile strength	tensile strength	Yield	ASTM D412	53.8	MPa
elongation	Break	ASTM D412	220	%
tensile strength	100%Strain	ASTM D412	12.4	MPa
	tensile strength	300%Strain	ASTM D412	24.1	MPa
	tensile strength	tensile strength	Yield	ASTM D412	52.6	MPa
elongation	Break	ASTM D412	450	%
Permanent compression deformation		ASTM D395B	29	%
Shore hardness		ASTM D2632	32	%
tensile strength	100%Strain	ASTM D412	3.96	MPa
	tensile strength	300%Strain	ASTM D412	6.00	MPa
	tensile strength	tensile strength	Yield	ASTM D412	50.3	MPa
elongation	Break	ASTM D412	640	%
Permanent compression deformation		ASTM D395B	26	%
Shore hardness		ASTM D2632	39	%
tensile strength	100%Strain	ASTM D412	19.7	MPa
	tensile strength	300%Strain	ASTM D412	38.4	MPa
	tensile strength	tensile strength	Yield	ASTM D412	56.7	MPa
elongation	Break	ASTM D412	400	%
Permanent compression deformation		ASTM D395B	35	%
Shore hardness		ASTM D2632	44	%
tensile strength	100%Strain	ASTM D412	33.1	MPa
tensile strength	tensile strength	Yield	ASTM D412	52.4	MPa
elongation	Break	ASTM D412	240	%
Permanent compression deformation		ASTM D395B	36	%
Shore hardness		ASTM D2632	45	%
tensile strength	100%Strain	ASTM D412	3.45	MPa
	tensile strength	300%Strain	ASTM D412	6.21	MPa
	tensile strength	tensile strength	Yield	ASTM D412	51.7	MPa
elongation	Break	ASTM D412	700	%
Shore hardness		ASTM D2632	40	%
tensile strength	100%Strain	ASTM D412	5.38	MPa
	tensile strength	300%Strain	ASTM D412	9.10	MPa
	tensile strength	tensile strength	Yield	ASTM D412	46.4	MPa
elongation	Break	ASTM D412	650	%
Permanent compression deformation		ASTM D395B	30	%
Shore hardness		ASTM D2632	35	%
elongation	Break	ASTM D412	430	%
Permanent compression deformation		ASTM D395B	33	%
Shore hardness		ASTM D2632	32	%
elongation	Break	ASTM D412	650	%
Permanent compression deformation		ASTM D395B	40	%
Shore hardness		ASTM D2632	50	%
tensile strength	100%Strain	ASTM D412	10.9	MPa
	tensile strength	300%Strain	ASTM D412	22.7	MPa
	tensile strength	tensile strength	Yield	ASTM D412	59.1	MPa
elongation	Break	ASTM D412	520	%
tensile strength	Yield	ASTM D412	55.7	MPa
elongation	Break	ASTM D412	570	%
Permanent compression deformation		ASTM D395B	24	%
tensile strength	100%Strain	ASTM D412	4.14	MPa
	tensile strength	300%Strain	ASTM D412	7.14	MPa
		tensile strength	100%Strain	ASTM D412	4.31	MPa
			tensile strength	300%Strain	ASTM D412	7.41	MPa
				tensile strength	Yield	ASTM D412	51.7	MPa
					tensile strength	100%Strain	ASTM D412	5.14	MPa
						tensile strength	300%Strain	ASTM D412	8.45	MPa
						tensile strength	tensile strength	Yield	ASTM D412	53.5	MPa
Permanent compression deformation		ASTM D395B	29	%
Shore hardness		ASTM D2632	28	%
tensile strength	100%Strain	ASTM D412	3.96	MPa
	tensile strength	300%Strain	ASTM D412	6.00	MPa
	tensile strength	tensile strength	Yield	ASTM D412	50.3	MPa
elongation	Break	ASTM D412	640	%
Permanent compression deformation		ASTM D395B	26	%
Shore hardness		ASTM D2632	39	%
tensile strength	100%Strain	ASTM D412	7.24	MPa
tensile strength	tensile strength	300%Strain	ASTM D412	11.4	MPa
elongation	Break	ASTM D412	640	%
Permanent compression deformation		ASTM D395B	25	%
Shore hardness		ASTM D2632	30	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
compressive strength	5%Strain	ASTM D695	1.91	MPa
compressive strength	compressive strength	10%Strain	ASTM D695	7.82	MPa
tensile strength	Break	ASTM D638	17.0	MPa
elongation	Break	ASTM D638	890	%
compressive strength	15%Strain	ASTM D695	12.6	MPa
	compressive strength	5%Strain	ASTM D695	0.972	MPa
		compressive strength	10%Strain	ASTM D695	3.37	MPa
			compressive strength	15%Strain	ASTM D695	5.58	MPa
			compressive strength	compressive strength	25%Strain	ASTM D695	8.56	MPa
thermosetting	Test Condition	Test Method	Test Result	Test Unit
storage stability			3.0to4.0	min
stripping time	100°C		20	min
Post curing time	100°C		16	hr
	Post curing time	22°C		72	hr
	Post curing time	Post curing time	99°C		16	hr
storage stability			2.0to3.0	min
stripping time	100°C		20	min
storage stability			10to12	min
Thermosetting mixed viscosity	70°C	ASTM D2393	1000	cP
stripping time			45	min
Post curing time	93°C		16	hr
storage stability			5.0to8.0	min
stripping time	100°C		30	min
Post curing time	100°C		16	hr
Post curing time	Post curing time	96°C		16	hr
storage stability			3.0to5.0	min
	storage stability			9.0to13	min
	storage stability	storage stability			3.0	min
stripping time			30	min
Post curing time	96°C		16	hr
Post curing time	Post curing time	100°C		4.0	hr
storage stability			2.5	min
stripping time	100°C		25	min
storage stability			10	min
Post curing time	100°C		16	hr
storage stability			6.0to7.0	min
stripping time	104°C		25	min
Post curing time	22°C		72	hr
Post curing time	Post curing time	100°C		16	hr
storage stability			3.0to6.0	min
stripping time	100°C		20	min
Post curing time	100°C		4.0	hr
stripping time	100°C		40to50	min
stripping time	stripping time	100°C		15	min
Post curing time	100°C		3.0	hr
Post curing time	Post curing time	100°C		16	hr
storage stability			9.5	min
stripping time	100°C		30to40	min
Post curing time	100°C		16	hr
storage stability			2.5	min
stripping time	100°C		24	min
Post curing time	100°C		16	hr
storage stability			6.0	min
stripping time			30	min
stripping time	stripping time	100°C		30	min
Post curing time	100°C		16	hr
storage stability			3.5to5.0	min
stripping time			30	min
storage stability			9.0to13	min
stripping time	100°C		30	min
Post curing time	100°C		16	hr
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D1505	1.22	g/cm³
Shrinkage rate	MD	ASTM D955	1.4	%
density		ASTM D1505	1.16	g/cm³
	density		ASTM D1505	1.22	g/cm³
	density	density		ASTM D1505	1.18	g/cm³
Shrinkage rate	MD	ASTM D955	1.1	%
density		ASTM D1505	1.20	g/cm³
density	density		ASTM D1505	1.23	g/cm³
Shrinkage rate	MD	ASTM D955	1.3	%
density		ASTM D1505	1.25	g/cm³
	density		ASTM D1505	1.20	g/cm³
		density		ASTM D1505	1.16	g/cm³
			density		ASTM D1505	1.23	g/cm³
				density		ASTM D1505	1.22	g/cm³
				density	density		ASTM D1505	1.21	g/cm³
Shrinkage rate	MD	ASTM D955	1.5	%
density		ASTM D1505	1.22	g/cm³
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	ShoreD	ASTM D2240	61
	Shore hardness	ShoreA	ASTM D2240	81
		Shore hardness	ShoreA	ASTM D2240	80
			Shore hardness	ShoreA	ASTM D2240	92
				Shore hardness	ShoreA	ASTM D2240	70
					Shore hardness	ShoreD	ASTM D2240	80
						Shore hardness	ShoreA	ASTM D2240	95
							Shore hardness	ShoreD	ASTM D2240	71
								Shore hardness	ShoreA	ASTM D2240	73
									Shore hardness	ShoreD	ASTM D2240	71
										Shore hardness	ShoreA	ASTM D2240	85
											Shore hardness	ShoreD	ASTM D2240	50
												Shore hardness	ShoreA	ASTM D2240	80
													Shore hardness	ShoreA	ASTM D2240	84
														Shore hardness	ShoreA	ASTM D2240	80
														Shore hardness	Shore hardness	ShoreA	ASTM D2240	91

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.