| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.47 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.50to1.1 % |
| Shrinkage rate | | ISO 294-4 | 0.10to0.30 % |
| melt viscosity | | ISO 11443 | 220 Pa·s |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO 527-2 | 2.5 % |
| Flexural modulus | | ISO 178 | 7500 MPa |
| bending strength | | ISO 178 | 190 MPa |
| Tensile modulus | | ISO 527-2 | 10000 MPa |
| tensile strength | | ISO 527-2 | 125 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 8.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 22 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 160 °C |
| melting temperature | | ISO 11357-3 | 225 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.