Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ISO60 | 0.70到0.85 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.20到0.45 % |
| Water absorption rate | | ISO62 | <0.20 % |
| PostShrinkage | | ISO2577 | <0.050 % |
| density | | ISO1183 | 1.80到2.00 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC60695-2-12 | 850 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 875 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 5.0-6.0 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 3.0到4.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Injection | ISO527-2 | 14000到17000 MPa |
| Tensile stress | Injection | ISO527-2 | 50.0到70.0 MPa |
| Flexural modulus | Injection | ISO178 | 12000到15000 MPa |
| Bending stress | Injection | ISO178 | 100到140 MPa |
| compression stress | | ISO604 | 150到200 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC60243-1 | 15到20 kV/mm |
| | IEC60250 | 4.005.00 |
| | IEC60250 | 4.005.00 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| arc resistance | | ASTMD495 | PLC 4 |
| Surface Resistivity | | IEC60093 | 1.0E+14到1.0E+15 ohms |
| Volume resistivity | | IEC60093 | 1.0E+14到1.0E+15 ohms·cm |
| CTI | | IEC60112 | >550 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | >200 °C |
| | ISO75-2/C | >180 °C |
| | ISO11359-2 | 5.0E-5到6.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.40到0.60 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.