Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.02 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 6.0 g/10min |
| Shrinkage rate | | | 0.20to0.80 % |
| Water absorption rate | | ISO 62 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO 2039-2 | 55 |
| Shore hardness | | ISO 868 | 71 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ISO 3537 | 0.50 % |
| transmissivity | | ISO 3537 | 90.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2/5 | 27.0 MPa |
| Tensile strain | Break | ISO 527-2/5 | 200 % |
| Flexural modulus | | ISO 178 | 1200 MPa |
| bending strength | | ISO 178 | 37.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Complete Break | ISO 179 | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | Complete Break | ISO 179 | 100 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 57.0 °C |
| vicat | | ISO 306/A50 | 82.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.