PA66/PTFE LNP™ LUBRICOMP™ RFL-4038
109
- Properties:wear resistantThermal stabilityFiller: Glass fiber reinf10% filler by weight
- Usages:Plastic bag
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO62 | 0.97 % | |
| Shrinkage rate | ASTMD955 | 0.50to0.70 % | |
| ASTMD955 | 1.0to3.0 % | ||
| Water absorption rate | ASTMD570 | 0.64 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTMD638 | 5640 Mpa | |
| ISO527-2/1 | 5500 Mpa | ||
| tensile strength | ASTMD638 | 107 Mpa | |
| Tensile stress | ISO527-2/5 | 103 Mpa | |
| elongation | ASTMD638 | 2.8 % | |
| Tensile strain | ISO527-2/5 | 2.7 % | |
| Flexural modulus | ASTMD790 | 5300 Mpa | |
| ISO178 | 5020 Mpa | ||
| Bending stress | ISO178 | 159 Mpa | |
| Bending strength 5 | ASTMD790 | 165 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam notch impact strength 6 | ISO180/1A | 4.9 kJ/m² | |
| Unscented Izod Impact Strength 5 | ISO180/1U | 25 kJ/m² | |
| Dart impact equipped with measuring instruments | ASTMD3763 | 6.58 J | |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 1.56 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature 7 | ISO75-2/Af | 240 °C | |
| ASTMD696 | 4.7E-05 cm/cm/°C | ||
| ASTMD696 | 8.6E-05 cm/cm/°C | ||
| ASTMD648 | 260 °C | ||
| Hot deformation temperature 7 | ISO75-2/Bf | 257 °C | |
| ASTMD648 | 246 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.