PPS A604 TORAY JAPAN

265

Form：Granules | Grade：Injection grade

Properties:

High temperature resistanGlass fiber reinforcedFlame retardant

Typical Applications:

sporting goodsAutomotive sectorElectronic fieldElectrical field

Supplier(8)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	sporting goods \| Automotive sector \| Electronic field \| Electrical field
Properties:	High temperature resistan \| Glass fiber reinforced \| Flame retardant

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
Color			米色.黑色
characteristic			40%加纤.增强.高韧性
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	60	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.200mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C	ISO 178	300	Mpa
shear strength	23°C	JISK7214	80.0	Mpa
Friction coefficient			0.24
Taber abraser	1000Cycles	ISO 9352	50.0	mg
Bending modulus	23°C	ISO 178	14500	Mpa
Tensile strain	Break,23°C	ISO 527-2	2.0	%
tensile strength	Yield,23°C	ISO 527-2	205	Mpa
bending strength		ASTM D790/ISO 178	300	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	14.5	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	122
tensile strength		ASTM D638/ISO 527	205	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	2	%
Charpy Notched Impact Strength		ASTM D256/ISO 179	60	kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	12	kg·cm/cm(J/M)ft·lb/in
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	260	°C
Melting temperature		ISO 11357-3	278	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2.3E-05	cm/cm/°C
	Linear coefficient of thermal expansion	TD	ISO 11359-2	3.5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ASTM D696/ISO 11359	2.3	mm/mm.℃
Melting temperature			278	℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	>260	℃（℉）
Combustibility (rate)		UL 94	V-0
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ISO 62	0.020	%
Shrinkage rate	MD:3.00mm4	Internal Method	0.20	%
Shrinkage rate	Shrinkage rate	TD:3.00mm2	Internal Method	0.80	%
Water absorption rate		ASTM D570/ISO 62	0.02	%
Shrinkage rate		ASTM D955	0.2	%
density		ASTM D792/ISO 1183	1.66
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1E+16	ohms·cm
Dielectric strength		IEC 60243-1	24	KV/mm
Dielectric constant	23°C,1MHz	IEC 60250	3.60
Dissipation factor	23°C,1MHz	IEC 60250	2E-03
Volume resistivity		ASTM D257/IEC 60093	1014	Ω.cm
Dielectric constant		ASTM D150/IEC 60250	3.6
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	122
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
BarFlowLength	320°C,1.00mm	Internal Method	120	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.