Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 2.8 g/10 min |
| Shrinkage rate | | ASTM D955 | 0.20 - 0.60 % |
| Water absorption rate | | ISO 62 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 97 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO 489 | 1.490 |
| transmissivity | | ASTM D1003 | 92.0 % |
| Haze ratio | | ASTM D1003 | 0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 70.0 Mpa |
| Tensile strain | | ISO 527-2 | 6.0 % |
| Flexural modulus | | ISO 178 | 3300 Mpa |
| bending strength | | ISO 178 | 103 Mpa |
| compression stress | | ISO 604 | 117 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/2U | 11 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | > 1.0E+14 ohms |
| Volume resistivity | | ASTM D257 | > 1.0E+15 ohms·cm |
| dielectric strength | | ASTM D149 | 20 KV/mm |
| dielectric constant | | ASTM D150 | 3.70 |
| Dissipation Factor | | ASTM D150 | 0.040 |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 85 to 90 °C |
| drying time | | | 2.0 to 4.0 hr |
| Processing (melt) temperature | | | 230 to 250 °C |
| Temperature | | | 80 to 90 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 103 °C |
| Heat distortion temperature | | ISO 75-2/A | 100 °C |
| vicat | | ISO 306/B | 108 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6.5E-5 cm/cm/°C |
| specific heat | | | 2090 J/kg/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.