PCT Thermx® TE4004 CELANESE USA
0
- Properties:Fillerfiberglass flakes40%filler by weight
- Usages:Application in the automotive field
CompareTechnical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 240 °C |
| melting temperature | ISO 11357-3 | 285 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.51 g/cm³ | |
| shrinkage rate | TD | ISO 294-4 | 0.90 % |
| MD | ISO 294-4 | 0.30 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 38 kV/mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile modulus | ISO 527-2/1A/1 | 9000 MPa | |
| bending strength | 23°C | ISO 178 | 160 MPa |
| tensile strength | Break | ISO 527-2/1A/5 | 105 MPa |
| Tensile strain | Break | ISO 527-2/1A/5 | 2.3 % |
| flexural modulus | 23°C | ISO 178 | 8000 MPa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.