Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | Resin | | 100 |
| Thermosetting components | Hardener | | 按重量计算的混合比:8.8 |
| Thermosetting components | | | 6.0to12 min |
| Thermosetting components | | | 45to60 min |
| Thermosetting components | | | 170 hr |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.07 g/cm³ |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Curing Time | | | 3.0 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 80 |
| Shore hardness | | ASTM D2240 | 80 |
| Shore hardness | | ASTM D2240 | 75 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| AbrasionIndex-NBS | | | 110 |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D412 | 2.59 MPa |
| tensile strength | | ASTM D412 | 2.76 MPa |
| tensile strength | | ASTM D412 | 4.31 MPa |
| tensile strength | | ASTM D412 | 3.79 MPa |
| tensile strength | | ASTM D412 | 4.31 MPa |
| Shore hardness | | ASTM D2632 | 70 % |
| tensile strength | | ASTM D412 | 2.76 MPa |
| tensile strength | | ASTM D412 | 20.7 MPa |
| tensile strength | | ASTM D412 | 17.9 MPa |
| tensile strength | | ASTM D412 | 11.7 MPa |
| elongation | | ASTM D412 | 650 % |
| elongation | | ASTM D412 | 800 % |
| elongation | | ASTM D412 | 780 % |
| tear strength | | ASTM D470 | 5.3 kN/m |
| tear strength | | ASTM D470 | 11 kN/m |
| tear strength | | ASTM D470 | 12 kN/m |
| compression set | | ASTM D395B | 45 % |
| aging | Test Condition | Test Method | Test Result |
|---|
| volume change | | ASTM D471 | 180 % |
| volume change | | ASTM D471 | 25 % |
| volume change | | ASTM D471 | 60 % |
| volume change | | ASTM D471 | 500 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare