'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPO SE1-802 SABIC INNOVATIVE US
143
Form：Granules | Grade：Injection grade
Properties:
High temperature resistanHydrolysis resistance
Typical Applications:
Automotive componentsHousehold appliances
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Automotive components | Household appliances |
| Properties: | High temperature resistan | Hydrolysis resistance |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 15 | kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 49.7 | J |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.5mm | UL 94 | V-1 | |
| 6.0mm | UL 94 | V-0 | ||
| RadiantPanelListing(UL) | UL 94 | RP100 | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | ISO 178 | 2560 | Mpa | |
| 100mmSpan6 | ASTM D790 | 2400 | Mpa | |
| 50.0mmSpan5 | ASTM D790 | 2700 | Mpa | |
| Tensile strain | Break | ISO 527-2/50 | 21 | % |
| elongation | Break | ASTM D638 | 15 | % |
| Tensile strain | Yield | ISO 527-2/50 | 4.3 | % |
| elongation | Yield | ASTM D638 | 4.0 | % |
| tensile strength | Break | ISO 527-2/50 | 50.8 | Mpa |
| Break | ASTM D638 | 53.1 | Mpa | |
| Yield | ISO 527-2/50 | 61.3 | Mpa | |
| bending strength | ISO 178 | 99.5 | Mpa | |
| Yield,50.0mmSpan5 | ASTM D790 | 100 | Mpa | |
| Yield,100mmSpan6 | ASTM D790 | 98.0 | Mpa | |
| Tensile modulus | ASTM D638 | 2500 | Mpa | |
| ISO 527-2/1 | 2670 | Mpa | ||
| tensile strength | Yield | ASTM D638 | 65.0 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| RTI Str | UL 746 | 110 | °C | |
| RTI Imp | UL 746 | 105 | °C | |
| RTI Elec | UL 746 | 110 | °C | |
| Linear coefficient of thermal expansion | TD：-40to40°C | ASTME831 | 8.8E-05 | cm/cm/°C |
| MD：-40to40°C | ASTME831 | 8E-05 | cm/cm/°C | |
| Vicat softening temperature | -- | ISO 306/B120 | 135 | °C |
| -- | ISO 306/B50 | 132 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 115 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTM D648 | 118 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTM D648 | 113 | °C | |
| 0.45MPa,Unannealed,100mmSpan | ISO 75-2/Be | 129 | °C | |
| 0.45MPa,Unannealed,3.20mm | ASTM D648 | 127 | °C | |
| 0.45MPa,Unannealed,6.40mm | ASTM D648 | 129 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | 24hr | ASTM D570 | 0.060 | % |
| Outdoor applicability | UL 746C | f1 | ||
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 8.5 | g/10min |
| Melt Volume Flow Rate (MVR) | 280°C/5.0kg | ISO 1133 | 8.70 | cm3/10min |
| Shrinkage rate | MD：3.20mm | Internal Method | 0.50-0.70 | % |
| TD2 | Internal Method | 0.50-0.70 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dielectric constant | 50Hz | ASTM D150 | 2.52 | |
| 60Hz | ASTM D150 | 2.52 | ||
| 1MHz | ASTM D150 | 2.46 | ||
| Dissipation factor | 50Hz | ASTM D150 | 3.4E-03 | |
| 60Hz | ASTM D150 | 3.4E-03 | ||
| Dielectric strength | 3.20mm,inOil | ASTM D149 | 18 | KV/mm |
| Volume resistivity | ASTM D257 | 2.3E+16 | ohms·cm | |
| Surface resistivity | ASTM D257 | >1.0E+15 | ohms | |
| Dissipation factor | 1MHz | ASTM D150 | 2.1E-03 | |
| Arc resistance | ASTM D495 | PLC6 | ||
| Compared to the anti leakage trace index | CTI | UL 746 | PLC 1 | |
| High voltage arc tracing rate | HVTR | UL 746 | PLC 4 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.