Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Shrinkage rate | | ASTM D955 | 1.0 % |
Water absorption rate | | ASTM D570 | 0.020 % |
density | | ASTM D792 | 1.96 g/cm³ |
Shrinkage rate | | ASTM D955 | 0.25 % |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | R-Scale | ASTM D785 | 121 |
Rockwell hardness | M-Scale | ASTM D785 | 100 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-0 |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | | ASTM D638 | 135 MPa |
elongation | Break | ASTM D638 | 0.90 % |
Flexural modulus | | ASTM D790 | 17500 MPa |
bending strength | | ASTM D790 | 210 MPa |
compressive strength | | ASTM D695 | 150 MPa |
Poisson's ratio | | | 0.34 |
Tensile modulus | | ASTM D638 | 18500 MPa |
coefficient of friction | Steel - Dynamic | ASTM D1894 | 0.35 |
coefficient of friction | Steel - Static | ASTM D1894 | 0.35 |
elongation at break | | ASTM D790 | 1.6 % |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ASTM D256 | 80 J/m |
Suspended wall beam without notch impact strength | | ASTM D256 | 340 J/m |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Dissipation Factor | | ASTM D150 | 6E-03 |
arc resistance | | ASTM D495 | 180 sec |
Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 2 |
Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
dielectric strength | | ASTM D149 | 16 kV/mm |
dielectric constant | | ASTM D150 | 5.00 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ASTM D648 | 265 °C |
Linear coefficient of thermal expansion | | ASTM D696 | 1.7E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTM D696 | 1.7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.