Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.38to1.42 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.030to0.40 % |
| flow ratio | | 内部方法 | 230 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 97 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Limiting Oxygen Index | | ASTM D2863 | 35 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2410 MPa |
| tensile strength | Yield | ASTM D638 | 40.0 MPa |
| Flexural modulus | | ASTM D790 | 2140 MPa |
| bending strength | | ASTM D790 | 65.5 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 53 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 960 J/m |
| Dart impact | | ASTM D4226 | 89.0 J/cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ASTM D648 | 72.0 °C |
| Hot deformation temperature (HDT) | | ASTM D648 | 70.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare