Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.14 g/cm³ |
| density | | | 0.070 % |
| | | 800 mPa·s |
| | | 6000 mPa·s |
| density | | | 0.958 g/cm³ |
| density | | | 1.07 g/cm³ |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Resin | | 按重量计算的混合比:100 |
| Hardener | | 按重量计算的混合比:120 |
| STORAGE STABILITY | | | 40 min |
| STORAGE STABILITY | | | 8.0 min |
| Thermosetting mixed viscosity | | | 2000 cP |
| Thermosetting mixed viscosity | | | 320 cP |
| stripping time | | | 10000 min |
| stripping time | | | 240 min |
| GelTime | | | 1.5 hr |
| GelTime | | | 0.3 hr |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| LinearShrinkage | | | 1.4 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore A | | 80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| PeakExotherm | | | 69 °C |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | | 13.8 MPa |
| compression set | | | 10 % |
| elongation | Break | | 160 % |
| tear strength | | | 20.8 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | | >1.0E+15 ohms |
| Volume resistivity | | | 7.2E+14 ohms·cm |
| dielectric strength | | | 26 kV/mm |
| dielectric constant | | | 3.40 |
| Dissipation Factor | | | 0.017 |
| InsulationResistance | | | >2.5E+13 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | | 3.8E-04 cm/cm/°C |
| thermal conductivity | | | 0.30 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.