| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.51 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.035 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| Shore hardness | | ASTM D2240 | 82 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 2410 MPa |
| bending strength | Yield | ASTM D790 | 75.8 MPa |
| compressive strength | | ASTM D695 | 78.6 MPa |
| shear strength | | ASTM D732 | 63.6 MPa |
| Tensile modulus | | ASTM D638 | 2760 MPa |
| tensile strength | Yield | ASTM D638 | 52.4 MPa |
| elongation | Break | ASTM D638 | 37 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 53to110 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 2.4E+15 ohms·cm |
| dielectric strength | | ASTM D149 | 60 kV/mm |
| dielectric constant | | ASTM D150 | 2.97 |
| dielectric constant | | ASTM D150 | 2.91 |
| dielectric constant | | ASTM D150 | 2.85 |
| Dissipation Factor | | ASTM D150 | 0.012 |
| Dissipation Factor | | ASTM D150 | 0.015 |
| Dissipation Factor | | ASTM D150 | 0.017 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 100 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 8E-05 cm/cm/°C |
| specific heat | | ASTMC351 | 920 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.092 W/m/K |
| vicat | | ASTM D1525 | 41.1 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.