Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.11 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.050to0.20 % |
| Shrinkage rate | | ASTM D955 | 0.40to0.60 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256A | 43 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 7720 MPa |
| tensile strength | Break | ASTM D638 | 78.6 MPa |
| elongation | Break | ASTM D638 | 1.5 % |
| Flexural modulus | | ASTM D790 | 8620 MPa |
| bending strength | | ASTM D790 | 123 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 1.0E+3到1.0E+5 ohms |
| Volume resistivity | | ASTM D257 | 1.0E+3到1.0E+5 ohms·cm |
| StaticDecay | | | 2 msec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 102 °C |
| Heat distortion temperature | | ASTM D648 | 97.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.