PA WINDFORM® SP
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 1.11 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 6220 MPa | |
| tensile strength | ISO 527-2 | 76.1 MPa | |
| Tensile strain | Break | ISO 527-2 | 11 % |
| Flexural modulus | ISO 14125 | 4650 MPa | |
| bending strength | ISO 14125 | 120 MPa | |
| Flexural modulus | 4200 MPa/g/cm³ | ||
| FlexuralStrength | 109 MPa/g/cm³ | ||
| UltimateTensileStrength | 68.8 MPa/g/cm³ | ||
| Tensile modulus | 5620 MPa/g/cm³ |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 5.8 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179 | 29 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | <1.0E+8 ohms | |
| Volume resistivity | ASTM D257 | <1.0E+8 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648B | 187 °C | |
| vicat | ASTM D15252 | 190 °C | |
| melting temperature | ISO 11357 | 193 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.