Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.05 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 10 g/10min |
| Shrinkage rate | | ASTMD955 | 0.50to0.80 % |
| density | | ASTMD792 | 1.05 g/cm³ |
| Shrinkage rate | | ASTMD995 | 0.50-0.80 % |
| | ASTMD1238 | 4.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 110 R |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTMD638 | 34.5 MPa |
| tensile strength | Break | ASTMD638 | 26.9 MPa |
| Impact strength of cantilever beam gap | | ASTMD256 | 320 J/m |
| elongation | Yield | ASTMD638 | 8.0 % |
| elongation | Break | ASTMD638 | 15 % |
| Flexural modulus | | ASTMD790 | 1720 MPa |
| bending strength | | ASTMD790 | 55.2 MPa |
| tensile strength | | ASTMD638 | 44.8 MPa |
| tensile strength | | ASTMD638 | 31.7 MPa |
| elongation at break | | ASTMD638 | 3.0 % |
| elongation at break | | ASTMD638 | 26 % |
| bending strength | | ASTMD790 | 68.9 MPa |
| Flexural modulus | | ASTMD790 | 2140 MPa |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Mouth size | | | 30-60 % |
| Mouth depth | | | 0.00381-0.00508 cm |
| Screw speed | | | 30-60 rpm |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 190 J/m |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| fire rating | | UL-94 | 1.50mm HB |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 82.2 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.