PPO NH7010 BK1005 SABIC INNOVATIVE SHANGHAI

112

Form：Granules | Grade：Injection grade

Properties:

High mobilityChemical resistanceHigh rigidity

Typical Applications:

Electrical applicationselectrical equipment

Supplier(2)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical applications \| electrical equipment
Properties:	High mobility \| Chemical resistance \| High rigidity

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	38.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	2.0 mm	UL 94	5VA
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 50.0 mm Span4	ASTM D790	102	Mpa
bending strength	bending strength	--5,6	ISO 178	109	Mpa
elongation	Yield	ISO 527-2/50	4.9	%
elongation	elongation	Yield3	ASTM D638	5.2	%
tensile strength	Break	ISO 527-2/50	63.0	Mpa
	tensile strength	Break3	ASTM D638	49.0	Mpa
		tensile strength	Yield	ISO 527-2/50	69.0	Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	68.0	Mpa
Tensile modulus	--	ISO 527-2/1	2500	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2250	Mpa
Bending modulus	--5	ISO 178	2520	Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2470	Mpa
elongation	Break	ISO 527-2/50	8.4	%
elongation	elongation	Break3	ASTM D638	41	%
injection	Test Condition	Test Method	Test Result	Test Unit
Back pressure			0.300 to 0.700	Mpa
Screw speed			20 to 100	rpm
Suggested maximum moisture content			0.020	%
Suggested injection volume			30 to 70	%
Temperature at the rear of the barrel			265 to 315	°C
Temperature in the middle of the barrel			275 to 320	°C
Temperature at the front of the material cylinder			290 to 325	°C
Spray nozzle temperature			300 to 325	°C
Processing (melt) temperature			300 to 325	°C
Mold temperature			80 to 110	°C
drying temperature			110 to 120	°C
drying time			3.0 to 4.0	hr
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B120	162	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	8.2E-5	cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	161	°C
Vicat softening temperature	Vicat softening temperature	--	ASTM D15259	160	°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	139	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	139	°C
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	8.2E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	8.2E-5	cm/cm/°C
RTI Elec		UL 746	105	°C
RTI Imp		UL 746	105	°C
RTI		UL 746	105	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.050	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.25	%
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.80	%
Melt Volume Flow Rate (MVR)	300°C/5.0 kg	ISO 1133	10.0	cm3/10min
melt mass-flow rate	300°C/5.0 kg	ASTM D1238	10	g/10 min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
High voltage arc tracing rate		UL 746	PLC 4
Hot wire ignition		UL 746	PLC 0
Arc resistance		ASTM D495	PLC 6
Compared to the anti leakage trace index		UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PPO NH7010 BK1005 SABIC INNOVATIVE SHANGHAI

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index